NovaLene ® Polypropylene homopolymer (PP-H) sheets are a semi-crystalline, translucent polymer with high toughness and weather resistance properties. PPH sheets are non-polar, electrically insulated thermoplastic with 60 to 70% crystallinity. PP-H sheets have a density of 0.90 to 0.91 g/cm3, among the lowest densities for all plastics. PP-H has replaced a lot of traditional materials of construction, including metals, wood, and concrete, in a variety of applications as they are resistant to many chemicals and solvents, making them good for aggressive environments. Other NovaLene ® polypropylene sheets are made in 3 primary grades for application-based usage – in PP-Homopolymer (PP-H), PP-copolymer (PP-C) & PP Random Copolymer (PP-R).
Properties | Test Method | Unit | PP-H |
Specific gravity (ρ) | ISO 1183 | g/cm³ | 0.91 |
Max. permissible service temperature | Average | °C | 95 |
Lower permissible service temperature | – | °C | 5 |
Tensile strength at yield | ISO 527 | Mpa | >28 |
Tensile strength at break | ISO 527 | Mpa | >31 |
Elongation at yield | ISO 527 | % | ≥8 |
Elongation at break | ISO 527 | % | ≥80 |
Notch impact strength | ISO 179 | KJ/m2 | 9 |
Impact strength | ISO 179 | KJ/m2 | No Break |
Modulus of elasticity | ISO 527 | Mpa | 1700 |
Shore hardness | ISO 868 | Shore -D | 71 |
Vicat Softening Temperature | ISO 306 | °C | 105 |
Heat deflection temperature | ISO 306 | °C | 90 |
WhatsApp us
Thickness (mm) | Width × Length (m) | Packing |
0.2-1 | 1.5× 20 1.22 × 2.44 1.25 × 2 1.5 × 3 | 10 Rolls |
2 | 10 Rolls | |
3 | 10 Rolls | |
4 | 10 Rolls | |
5 | 4/5/6/8 nos | |
6 | 4/5/6/ nos | |
8 | 3/4/5 nos | |
10 | 1.22 × 2.44 1.22 × 2 1.22 × 3 1.5 × 3 | 2/3/4/5 nos |
12 | 2/3/4 nos | |
15 | 2/3 nos | |
20 | 1 nos | |
25 | 1 nos | |
30-200 | 1.25× 2 | 1 nos |
PROPERTIES OF PRODUCT | STANDARD | Data | Unit |
DENSITY | ISO – 1183 / ASTM 1505 | > 0.900 | g/cc |
MELT FLOW RATE (230°c/2.16 kg) | ISO – 1133 / ASTM D 1238 | 0.2-4.1 | Shore-D |
HARDNESS ( SHORE-D) | ASTM D 2240 | > 67 | Mpa |
TENSILE STRENGTH @ YIELD | ISO – 527 / ASTM D 638 Type-IV | ≥ 22 | % |
Elongation at Break | ISO – 527 / ASTM D 638 Type-IV | ≥ 30 | % |
Change in dimension (150⁰c) Longitudinal | – | ± 2 | % |
Temperature With Stand | – | 80+ | °C |
Featured List of Applications
Download Technicals
Featured List of Applications
Thickness (mm) | Width × Length (m) | Packing |
0.2-1 | 1.5× 20 1.22 × 2.44 1.25 × 2 1.5 × 3 | 10 Rolls |
2 | 10 Rolls | |
3 | 10 Rolls | |
4 | 10 Rolls | |
5 | 4/5/6/8 nos | |
6 | 4/5/6/ nos | |
8 | 3/4/5 nos | |
10 | 1.22 × 2.44 1.22 × 2 1.22 × 3 1.5 × 3 | 2/3/4/5 nos |
12 | 2/3/4 nos | |
15 | 2/3 nos | |
20 | 1 nos | |
25 | 1 nos | |
30-200 | 1.25× 2 | 1 nos |
PROPERTIES OF PRODUCT | STANDARD | Data | Unit |
DENSITY | ISO – 1183 / ASTM 1505 | > 0.900 | g/cc |
MELT FLOW RATE (230°c/2.16 kg) | ISO – 1133 / ASTM D 1238 | 0.2-4.1 | Shore-D |
HARDNESS ( SHORE-D) | ASTM D 2240 | > 67 | Mpa |
TENSILE STRENGTH @ YIELD | ISO – 527 / ASTM D 638 Type-IV | ≥ 22 | % |
Elongation at Break | ISO – 527 / ASTM D 638 Type-IV | ≥ 30 | % |
Change in dimension (150⁰c) Longitudinal | – | ± 2 | % |
Temperature With Stand | – | 80+ | °C |
Featured List of Applications
Download Technicals
Featured List of Applications
Thickness (mm) | Width × Length (m) | Packing |
0.2-1 | 1.5× 20 1.22 × 2.44 1.25 × 2 1.5 × 3 | 10 Rolls |
2 | 10 Rolls | |
3 | 10 Rolls | |
4 | 10 Rolls | |
5 | 4/5/6/8 nos | |
6 | 4/5/6/ nos | |
8 | 3/4/5 nos | |
10 | 1.22 × 2.44 1.22 × 2 1.22 × 3 1.5 × 3 | 2/3/4/5 nos |
12 | 2/3/4 nos | |
15 | 2/3 nos | |
20 | 1 nos | |
25 | 1 nos | |
30-200 | 1.25× 2 | 1 nos |
Properties | Test Method | Unit | PP-FR |
Specific gravity (ρ) | ISO 1183 | g/cm³ | 1.1 |
Max. permissible service temperature | – | °C | 5 to 100 |
Tensile strength at yield | ISO 527 | Mpa | 35 |
Tensile strength at break | ISO 527 | % | ≥400 |
Impact strength | ISO 179 | KJ/m2 | No Break |
Modulus of elasticity | ISO 527 | Mpa | 1300 |
Coef. Of linear therm. Expansion | DIN 53752 | k-1×10-4 | 1.5 |
Vicat Softening Temperature | ISO 306 | °C | 150 |
Shore hardness | ISO 868 | Shore -D | 70 |
Flammability | UL94 | – | V0 |
Featured List of Applications
Download Technicals
Featured List of Applications
Thickness (mm) | Width × Length (m) | Packing |
0.2-1 | 1.5× 20 1.22 × 2.44 1.25 × 2 1.5 × 3 | 10 Rolls |
2 | 10 Rolls | |
3 | 10 Rolls | |
4 | 10 Rolls | |
5 | 4/5/6/8 nos | |
6 | 4/5/6/ nos | |
8 | 3/4/5 nos | |
10 | 1.22 × 2.44 1.22 × 2 1.22 × 3 1.5 × 3 | 2/3/4/5 nos |
12 | 2/3/4 nos | |
15 | 2/3 nos | |
20 | 1 nos | |
25 | 1 nos | |
30-200 | 1.25× 2 | 1 nos |
Properties | Test Method | Unit | PP-2222 |
Specific gravity (ρ) | ISO 1183 | g/cm³ | 0.912 |
Max. permissible service temperature | – | °C | 5 to 100 |
Tensile strength at yield | ISO 527 | Mpa | 26 |
Tensile strength at break | ISO 527 | % | ≥400 |
Impact strength | ISO 179 | KJ/m2 | No Break |
Modulus of elasticity | ISO 527 | Mpa | 1200 |
Coef. Of linear therm. Expansion | DIN 53752 | k-1×10-4 | 1.5 |
Vicat Softening Temperature | ISO 306 | °C | 148 |
Shore hardness | ISO 868 | Shore -D | 67 |